– Natural rubber based automotive tubes.
– Natural rubber tubes for bicycle, 2-3 wheeler, Light moter vehicle, truck etc.
– Automobile extruded parts.
– Moulded rubber product & Other extruded product.
– Other extruded product.
– Low calandering, mixing and extrusion temperature.
– mproved penetration of fabric and cord. Lower swelling and shrinking during extrusion and calandering.
– Increased tack. Improved reversion and ageing performance of natural Rubber compounds (ozone, UV).
– Lower raw material costs.
|Acetone Extract||%||ASTM D297||9 – 15|
|Ash||%||ASTM D297||20 – 30|
|Carbon Black||%||ASTM D297||11 – 25|
|RHC By Difference||%||ASTM D297||42 min|
|Specific Gravity||–||ASTM D297||1.2 -1.3|
|Hardness||Shore A||ASTM D2240||55 – 65|
|Tensile Strength||kg/cm2||ASTM D412||30 min|
|Elongation at Break||%||ASTM D412||250 min|
|Mooney Viscosity||ML (1+4)@100ºC.||ASTM D1646||25 – 55|
|Volatile Matter||%||1 Max|
|20min @ 155ºC|